SLN-Kristall für Hochtemperatur-SAW

Vorteile von MgO:SLN
Niedriges Magnetfeld – geeignet für hochpräzisen und schnellen Phasenanpassungsprozess
20%-50% höhere Wärmeleitfähigkeit als normales MgO:LN
Hohe photorefraktive Schadensschwelle


  Jetzt Kontakt aufnehmen
Produktdetails

Nominally pure stoichiometric LiNbO 3 " Rolle = "Präsentation"> LiNbO 3 shows lower photorefractive damage resistance than congruent crystal; however, stoichiometric crystals doped with MgO of more than 1.8 mol. % exhibit no measurable photorefractive damage at 532 nm to intensities of as much as 8 MW / cm 2 " Rolle="Präsentation"> 8   MG / cm 2 . This remarkable damage resistance can be attributed not only to increased photoconductivity but also to decreased photogalvanic current. Stoichiometric mg : LiNbO 3 " Rolle = "Präsentation"> Mg : LiNbO 3 also demonstrates the shortest absorption edge, 302 nm, and a single-domain nature with low scattering losses.


Typische Anwendungen
Periodisch polarisiertes Gerät
THz-Gerät


Beschreibung

Wert

Absorptionskante (20 cm -1 )

303 ( c = 49,9)

Doppelbrechungsindex (633nm)

-0,0900 ( c = 50,0)

Elektrooptischer Koeffizient (pm/V)

R 61 = 9,89 ( c = 49,95)

Nichtlinearer Koeffizient (pm/V)

17,5 ( c = 49,8)

OH-Absorptionspeak/FWHM (cm -1 )

3465,5/2,9 ( c = 49,9)

Domäneninversionsspannung (kV/cm²)

0,8 ( c = 49,9)

Schadensschwelle

100 MW/ cm2 bei 532 nm

c in der Tabelle ist der Li 2 O-Gehalt des Kristalls